ASTM A179/A179M Seamless Cold-drawn Low-carbon Steel Tube supplied by Hebei K-Steel pipe Industry

 ASTM A179/A179M, from Hebei K-Steel Pipe Industry is a standard specification for ASTM A179seamless cold-drawn low-carbon steel tubes primarily used in tubular heat exchangers, condensers, and similar heat transfer equipment. It is widely valued for its high dimensional accuracy, smooth surface finish, and excellent thermal conductivity

Key Specifications and Grades

The standard covers tubes with an outside diameter (OD) ranging from 1/8 inch to 3 inches (3.2 mm to 76.2 mm). It typically includes two primary grades

  • Grade A: A standard grade with a minimum yield strength of 35 ksi (240 MPa), ideal for general industrial applications.
  • Grade C: A higher-strength version with a minimum yield strength of 47 ksi (325 MPa), suitable for more demanding high-pressure environments.Chemical and Mechanical PropertiesProperty                             RequirementCarbon Content              0.06% – 0.18% (ensures ductility and weldability)Manganese                      0.27% – 0.63%Tensile Strength              Min. 47 ksi (325 MPa)Hardness                          Max. 72 HRB (Rockwell Hardness, B scale)Thermal Treatment          Must be heat treated (annealed) at 1200°F (650°C) or higher after final cold drawingManufacturing and TestingAs specified by ASTM International, these tubes must be manufactured using the seamless process and finished through cold drawing. To ensure safety under high pressure, each tube must undergo rigorous quality checks:
  • Flattening and Flaring Tests: To verify the material's ductility and ability to withstand mechanical deformation.
  • Hydrostatic or NDT Test: Every tube is subjected to a water pressure test or a non-destructive electric test to ensure it is leak-free.
  • Dimensional Checks: Precise wall thickness and outer diameter tolerances are strictly maintained.Due to their reliability in varying temperatures and pressures, ASTM A179 tubes are essential in several sectors: Power Plants: In condensers and boiler feed-water heaters.
  • Petrochemical Industry: For refining and cooling processes in heat exchangers.
  • Marine Systems: Used in seawater cooling equipment due to its adaptability.
  • Sugar Mills & Distilleries: For various thermal processing needs.

Comments

Post a Comment

Popular posts from this blog

Key Requirements for Steel Pipes in The Fluid Transport Industry

  Requirement Category                  Details Mechanical Properties                        High yield strength, good ductility (elongation ≥ 20%), impact resistance                                                              (especially low-temperature toughness) Weldability                                            Easy field welding, weld strength matching base metal, HAZ toughness compliant Corrosion Resistance                         External coating required (e.g., 3LPE, FBE); internal lining or coating (cement         ...
Read more

API 5L X42 PSL2 Welded Line Pipe Supplied by Hebei K-Steel Pipe Industry

  API 5L X42 PSL2   welded line pipe is engineered for medium-pressure oil, gas, and water transmission lines where enhanced toughness, stricter chemical limits, and traceability are required.   Hebei K-Steel pipe industry   can Manufacture to   API   Specification   API 5CT , this pipe outperforms PSL1 in fracture resistance, weldability, and low-temperature performance — ideal for onshore and offshore projects with demanding service conditions. Key Features: 1) Excellent weldability and dimensional accuracy 2) Delivery conditions N, Q, or M available to optimize properties 3) Suitable for high-pressure and critical pipeline applications 4) Strict chemical and mechanical property control than PSL1
Read more

K-STEEL STEEL PIPE MANUFACTURE PROCESS SPECIFICATION

https://www.k-steels.com/K-STEEL-SEAMLESS-STEEL-PIPE-MANUFACTURE-PROCESS-SPECIFICATION-id46133655.html   Steel Making Equipments EAF/BOF, LF 2. Cont inuous Casting 3. Billet inspection and cutting Inspection item: heat no, length, marking, dimensions, surface quality 4. Rotary Hearth Furnace Equipment:Φ28m rotating furnace. According to the procedure 5. Piercing & rolling-Equipment: ROLL Machine. According to the procedure . 6.Stretch Reducing Equipment:reducing sizing mill. 7. Normalizing Equipment:Heat Treatment Furnace, C omputer A id C ontrol S ystem 8. Straightening pressure straightening machine pressure straightening 9. Sampling for pipe body La dle Analysis: 1/heat Product chemical composition ： 2/ heat Tensile test ： 1 PCS/ lot ≤ 100PCS Traceability marking (heat and lot number) is applied on the sample and then on the specimen. 10. Product chemical composition Laboratory equipment Spectroanalysis instrument Pro...
Read more